Failure analysis - Failures of ceramic materials

Auf einen Blick

Englischer Titel

Schadensanalyse - Schäden an keramischen Werkstoffen

Erscheinungsdatum
2024-06
Enddatum der Einspruchsfrist
2024-11-30
Herausgeber
Engl. VDI-Gesellschaft Materials Engineering
Zugehörige Handbücher
Seitenanzahl
28
Erhältlich in
Deutsch
Kurzreferat

This standard describes the different types of damage, the damage characteristics, the causes of damage and the damage processes in the event of damage to ceramic products. It provides a basic guide to identifying possible causes of failure and fracture outcomes. It gives an overview of forms of damage that occur in ceramic materials and explains basic elements of practical fractography. The focus is on causes of failure that occur at room temperature and medium temperatures. The causes of failure that occur primarily at very high temperatures - creep, oxidation, and corrosion - are not described. Damage caused by brittle fracture is therefore primarily described. Particular emphasis is placed on the procedure for identifying fracture initiation.

Inhaltsverzeichnis der Richtlinie ansehen

Richtlinie bestellen

Preis ab
91,10 EUR inkl. MwSt.
Bei DIN Media bestellen

FAQ

Bitte beachten Sie, dass die Einspruchsfrist bereits abgelaufen ist.

Stellen Sie Ihre Frage / Nehmen Sie Kontakt mit uns auf

Teilen