VDI 3822 Blatt 1.6 Failure analysis - Liquid-metal-induced crack formation

Auf einen Blick

Englischer Titel
Schadensanalyse - Flüssigmetallinduzierte Rissbildung
Erscheinungsdatum
2019-06
Herausgeber
Engl. VDI-Gesellschaft Materials Engineering
Zugehörige Handbücher
Seitenanzahl
50
Erhältlich in
Deutsch, Englisch
Kurzreferat

This standard provides information to help explain the causes of failure in the field of hot dip galvanising. With regard to quality assurance measures in the manufacturing chain, from the technical designer to the galvaniser, the standard may also help to prevent costly and the occurrence of sometimes dangerous errors. Among others, the standard describes the liquid metal induced cracking mechanism, process variables, the sphere of influence of construction and galvanising plant, and exemplary damages and consequential damages. Support and guidance on dealing with actual examples of failure can be found.

Inhaltsverzeichnis der Richtlinie ansehen

Richtlinie bestellen

Preis
125,90 EUR inkl. MwSt.
Bei Beuth bestellen

FAQ

Stellen Sie Ihre Frage / Nehmen Sie Kontakt mit uns auf

Teilen